1. High-temperature performance: Strength is maintained up to 1200℃ without degradation, and dec…

1、High Strength and High Hardness: Vickers hardness reaches 15-18 GPa, and flexural strength is …

1. Density: 3.2 g/cm³. 2. Flexural Strength: 600-800 MPa. 3. Vickers Hardness: 1450-1480 HV. …

1. Hardness: HV10 > 1450. 2. Flexural Strength: >850 MPa at room temperature, >350 MPa at 1200℃…

1. Hardness: HRA 92-94 (Vickers hardness approximately 1500 HV). 2. Bending Strength: ≥900 MPa.…

1. Superior mechanical properties: Bending strength >800 MPa (up to 1000 MPa or more), fracture …

1. Lighter than metal materials but with higher strength. 2. Excellent wear resistance and self…

1. Excellent mechanical properties: High flexural strength (above 800 MPa) and good toughness, c…

1. High strength: Hot-pressed silicon nitride is one of the hardest materials in the world, with…

1. High Pressure Resistance: Can withstand alternating loads exceeding 50 MPa, suitable for high…

1. Density: 3.20 g/cm³ (approximately 1/3 of steel). 2. Bending Strength: >900 MPa (high load c…

1. Dimensions: Common sizes include 20×20×9mm, 30×30×4mm, 50×50×0.32mm, 100×100×4mm, 107×107×4mm…