Hunan Kingda Ceramic Materials Co., Ltd.

Uniform Social Credit Code (USCC):91430103MA4L3C096L Changsha, Hunan, China http://www.kingdacera.com
Raw materials
Oxygenates, Zirconium Dioxide(ZrO2)

Powder preparation
-

Molding
-

Sintering process
-

processing technology
-

Category

Product Features

Product Line

Yttrium Stabilized Zirconia Balls

SKUKD-ZR
Online quote
Price MOQ Lead Time Customization Sample
Negotiable Negotiable Contact Supplier Yes Yes
Packing specification
Net weight Gross weight Dimension Remarks
Payment Terms
Shipping terms

Product Description

Model
-
Brand
KINGDA
Origin
• Offer certificat of origin
Port
Features

High density, high grinding efficiency, high hardness;

Compact Tetragonal Zirconia Polycrystalline (Y-TZP) to give the beads outstanding anti-corrosion and wear resistance;

Always keep the smooth surface and the good roundness;

Homogenous structure at high hardness;

15% superior to Ceria Stabilized beads in wear rate, proved by many tests.
Product Details

Material: 95% ZrO₂+5% Y₂O₃
Specific Density: ≥6.02 g/cm³
Size: 0.1-50mm
Model Number: KD-ZR
Brand: KINGDA

By special moulding and sintering technology, Kingda Y-TZP consists of yttrium stabilized zirconium oxide. Yttria Stabilized Zirconia (Y-TZP) is the strongest ceramic material we offer. Y-TZP is a purely tetragonal phase, fine grain material. This material offers the highest flexural strength of all Zirconia based materials. It gives significant advantages in the fields of resistance to wear and absence of contamination.

 

● Applications: 

   It is widely used for grinding, dispersing and polishing as following: inkjets inks, electronic slurries, raw material of battery, screen printing inks, coating, painting, pigment, ceramic and cosmetic and other nano particles products.  

 


● Package:

   25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.

 


● Storage:

   The grinding media should be stored in a dry and clean place.

Product parameters

Chemical Composition:

Composition

ZrO₂

Y₂O₃

Other

Content %

94.8±0.2

5.1±0.1

0.1%


Physical Properties:

Specific Gravity

g/cm³

Bulk Density

g/cm³

Hardness

Hv

Fracture Toughness

MPam1-2

Crushing Load

KN(Φ2.0mm)

Grain size
um

Wear loss
(%)

Sphericity
(%)

≥6.02

≥ 3.70

≥1250

9

≥20

≤0.5

≤0.08

≥98

 

● Ball Sizes :

Size(mm)

Size(mm)

Size(mm)

Size(mm)

Size(mm)

Φ0.08-0.12

Φ0.12-0.18

Φ0.18-0.22

Φ0.22-0.28

Φ0.28-0.35

Φ0.3-0.4

Φ0.4-0.5

Φ0.6-0.8

Φ0.8-1.0

Φ1.0-1.2

Φ1.2-1.4

Φ1.4-1.6

Φ1.6-1.8

Φ1.8-2.0

2.0-2.2

Φ2.2-2.4

Φ2.4-2.6

Φ2.6-2.8

Φ2.8-3.0

Φ3.0-3.2

Φ3.2-3.5

Φ4

Φ5

Φ6

Φ7

Φ8

Φ10

Φ12

Φ15

Φ17

Φ20

Φ25

Φ30

Φ40

Φ50

 

 Cylinder Sizes:

Size(mm)

Size(mm)

Size(mm)

Size(mm)

Size(mm)

Size(mm)

Φ3*3

Φ5*5

Φ7*7

Φ10*10

Φ12.7*12.7

Φ15*15

Product Gallery